Duplex 2205 Pipe Manufacturer in India
HOME → Our Products → Pipe → Duplex Steel Products → Duplex 2205 Pipe Manufacturer
Manufacturer of duplex 2205 seamless tube, high quality tuberia duplex 2205, duplex 2205 welded pipe, India, check tubi duplex 2205 Price in India.stockist of 2205 duplex stainless steel tubing in Mumbai,
Check tubo duplex 2205, alloy 2205 tubing suppliers, 22cr Duplex 2205 Pipe manufacturers, high quality 2205 duplex stainless steel tubes supplier and importer of 2205 duplex stainless tubing in India,
Table of Content
Manufacturer & Supplier of Duplex 2205 Pipe
The inside of 2205 Duplex Stainless Tubing, there are two stages in the micro structure of the tubing. When you buy Duplex 2205 stainless steel pipe, you get a microstructure that's made up of both ferrite and austenitic in an equal amount.
The chemical composition of 2205 Duplex Stainless Pipe consists of the elements that are employed in the following proportions: % chromium, 3 percent molybdenum, and around 5 to 6 % nickel. This stainless steel is also referred to as 22cr Duplex 2205 Pipe due to the amount of chromium contained in the alloy of this grade, which is a result of the content of chromium present in the alloy of this grade in terms of quantity.
The embrittlement of duplex 2205 seamless tube occurs when the material is subjected to temperatures exceeding 572°F for a prolonged period of time, even when the exposure is only for a short period of time. As a result, 2205 duplex pipe should not be utilised at temperatures above 572°F. Due to the presence of higher chromium, molybdenum, and nitrogen concentrations, 2205 duplex stainless steel tubes exhibit superior corrosion resistance in most conditions as compared to the more commonly used austenitic stainless steel grades 316 and 316L.
The inclusion of these three elements in greater levels in the duplex 2205 seamless pipe is also responsible for the alloy's increased resistance to pitting and crevice corrosion, even when the alloy is exposed to both oxidising and acidic solutions. Duplex 2205 pipe suppliers in Mumbai point out that this alloy has the potential to resist chloride ion stress related corrosion cracking, and that this is true even at temperatures that may reach up to approximately 302°F in the range of temperatures. The presence of ferrite in duplex 2205 welded pipe is what allows this stainless steel grade to operate better in caustic media-containing conditions than other stainless steel grades. We are well-known manufacturers, dealers, producers, and distributors of duplex 2205 pipe in India, among other countries.
What is Duplex 2205 pipe?
2205 duplex stainless steel tubing is the alloy type that is most extensively employed across a wide range of industrial applications. The 2205 duplex stainless tubing has been shown to have a high yield strength, which indicates that the yield strength of this alloy is twice or two times that of an austenitic stainless steel grade, which is the most commonly utilised in the industry today. In addition, the 2205 duplex stainless steel pipe has excellent fatigue strength as well as outstanding resistance to stress-related corrosion cracking, crevice corrosion, pitting, erosion corrosion, and general corrosion in extreme conditions, according to the manufacturer.
2205 duplex stainless steel Pipe Specification
Pipe Specifications |
|
Pipe Standard | DIN, JIS, ASTM, EN, GB, AISI, ASME Duplex 2205 Pipe Supplier |
Pipe Thickness | 0.3mm – 50 mm |
Duplex 2205 Welded Pipe size | 5.0 mm – 1219.2 mm |
Duplex 2205 Seamless Pipe Outer Diameter | 6.00 mm OD up to 250 mm OD, Sizes up to 12” NB |
Duplex 2205 EFW Pipe size | 5.0 mm – 1219.2 mm |
Duplex 2205 Welded Tube Size | 6.35 mm OD To 152 mm OD |
Duplex 2205 Seamless Tube Size | 3.35 mm OD To 101.6 mm OD, 15 NB to 150 NB IN |
Duplex 2205 tubing wall thickness | 0.020″ –0.220″ (special wall thicknesses available) |
Pipe & Tube Swg & Bwg | 10 Swg., 12 Swg., 14 Swg., 16 Swg., 18 Swg., 20 Swg. |
Duplex 2205 Pipe & Tube Finish | Polished, AP (Annealed & Pickled), BA (Bright & Annealed), MF, NO.1, NO.4, 2B, BA, HL, 8K, Mirror finish,etc |
Duplex 2205 Pipe Schedule | SCH 5, SCH10, SCH 40, SCH 80, SCH 80S, SCH 160, SCH XXS, SCH XS |
Duplex 2205 Pipe & Tube Length | Single Random, Double Random, Standard & Cut length |
Duplex 2205 Pipe & Tube Form | Round, Square, Hollow, Rectangular, Hydraulic, Coiled, Straight Pipes, “U” Shape, Pan Cake Coils etc. |
Duplex 2205 Pipe & Tube Type | Duplex 2205 Seamless / ERW/ EFW / Welded / Fabricated / CDW / DOM / CEW Pipe |
Duplex 2205 Pipe & Tube End | Plain End, Beveled End, Treaded Pipe. |
Duplex 2205 Tube Application | Boiler and Heatexchanger, Oil Tube, Fluid Tube, Gas Tube, |
Pipe Marking | All Duplex 2205 Pipes are marked as follows: Grade, Standard, OD, Thickness, Length, Heat No. (Or according to the customer’s request.) |
Pipe Value Added Service | Draw & Expansion as per required Size & Length, Polish (Electro & Commercial) Annealed & Pickled Bending, Machining Etc. |
Material Test Certificates (MTC) |
|
Specialized in |
|
We can also thread, cut, and groove Duplex 2205 Pipes & Tubes to meet your specifications. | |
22cr Duplex 2205 Pipe Chemical Composition
C | N | P | Si | Mn | Mo | Fe | Cr | S | Ni |
1.0 | 0.03 | 0.02 | 2.0 | 3.0 – 3.5 | 22.0 – 23.0 | 0.03 | 4.5 – 6.5 | 0.14 – 0.2 | Bal |
Duplex 2205 pipe Mechanical Properties
Pipe Density | Pipe Melting Point | Yield Strength (0.2%Offset) | 2205 Duplex SS Pipe Tensile Strength | Elongation |
7.8 g/cm3 | 1350 °C (2460 °F) | Psi – 80000 , MPa – 550 | Psi – 116000 , MPa – 800 | 15 % |
Equivalent Grades for Alloy 2205 UNS S32205 Pipe
| ASTM A450 | Hot rolled | Outside Diameter, mm | Tolerance, mm |
| OD≤101.6 | +0.4/-0.8 | ||
| 101.6＜OD≤190.5 | +0.4/-1.2 | ||
| 190.5＜OD≤228.6 | +0.4/-1.6 | ||
| Cold Drawn | Outside Diameter, mm | Tolerance, mm | |
| OD＜25.4 | ±0.10 | ||
| 25.4≤OD≤38.1 | ±0.15 | ||
| 38.1＜OD＜50.8 | ±0.20 | ||
| 50.8≤OD＜63.5 | ±0.25 | ||
| 63.5≤OD＜76.2 | ±0.30 | ||
| 76.2≤OD≤101.6 | ±0.38 | ||
| 101.6＜OD≤190.5 | +0.38/-0.64 | ||
| 190.5＜OD≤228.6 | +0.38/-1.14 | ||
| ASTM A530 & ASTM A335 | NPS | Outside Diameter, inch | Tolerance, mm |
| 1/8≤OD≤1-1/2 | ±0.40 | ||
| 1-1/2＜OD≤4 | ±0.79 | ||
| 4＜OD≤8 | +1.59/-0.79 | ||
| 8＜OD≤12 | +2.38/-0.79 | ||
| OD>12 | ±1% |